Help!! Audi A5 Sline Brilliant Black: Swirl Removal

[David at LC Pads]

Looks Great!

Glad you got it figured out!

Thanks for the update

[Theostoubos]

Thank you for the update,

I would really appreciate if you could elaborate a bit on what you think was the issue in your process.

Was it that the sanding marks were not removed during your compounding stage ? And FG400 was more effective that the previous compound ?

Or that your finishing step was not dialed in correctly and you could not finish swirl free.

To me it seems that you compounded again with FG400 and then refinish with SF 4000 ?

I would appreciate your response cause as soon as spring kicks in and the (-41 C ) goes away I will be polishing and opti coating my Audi Q7.

Theo

[WRAPT C5Z06]

I can't imagine being THAT much difference going from Uber compound to FG400. Maybe so...


Sent from my iPhone using Tapatalk

[foamingcarwash]

Thank you for the update,

I would really appreciate if you could elaborate a bit on what you think was the issue in your process.

Was it that the sanding marks were not removed during your compounding stage ? And FG400 was more effective that the previous compound ?

Or that your finishing step was not dialed in correctly and you could not finish swirl free.

To me it seems that you compounded again with FG400 and then refinish with SF 4000 ?

I would appreciate your response cause as soon as spring kicks in and the (-41 C ) goes away I will be polishing and opti coating my Audi Q7.

Theo

I can't imagine being THAT much difference going from Uber compound to FG400. Maybe so...


Sent from my iPhone using Tapatalk

Yes the FG400 was more effective then Uber Compound.. I used the same process as before just switched to the FG400..
FG400
SI1500 (PO83)
SF4000 (PO106)

[WRAPT C5Z06]

Yes the FG400 was more effective then Uber Compound.. I used the same process as before just switched to the FG400..

Interesting...